Project |
Units |
Average |
Maximum |
Minimum |
Several samples |
CV% |
| Quality unit area |
9/m2 |
190 |
195 |
181 |
10 |
0.020 |
| Thickness (Kpa) |
mm |
0.74 |
0.78 |
0.71 |
10 |
0.032 |
|
Stretching bands |
Tensile Strength (
Longitudinal
) |
N/5cm |
1635 |
1660 |
1570 |
6 |
0.024 |
| Elongation (Longitudinal) |
% |
24 |
26 |
23 |
6 |
0.048 |
| Tensile Strength (
Transverse
) |
N/5cm |
1985 |
2060 |
1860 |
6 |
0.033 |
| Elongation (
Transverse
) |
% |
22 |
23 |
21 |
6 |
0.037 |
| Gripping strength (
Longitudinal
) |
N |
1057 |
1080 |
1010 |
6 |
0.028 |
| Trapezoid tear strength (
Longitudinal
) |
N |
600 |
650 |
550 |
6 |
0.060 |
| Magnificently to break strength |
N |
/ |
|
|
|
|
| CBR to break strength |
N |
3957 |
4160 |
3620 |
6 |
0.050 |
| Vertical permeability coefficient |
cm/s |
0.0040 |
0.0052 |
0.0032 |
3 |
/ |
| Equivalent aperture O95 |
mm |
0.090 |
0.092 |
0.087 |
3 |
/ |
| Anti-UV capability |
After 500 hours after UV irradiation intensity of the original anti-intensity 80% |